Process for selective formation of II-VI group compound film

ABSTRACT

A process for selective formation of a II-VI group compound film comprises applying a compound film forming treatment, in a gas phase including a starting material for supplying the group II atoms of periodic table and a starting material for supplying the group VI atoms of periodic table, on a substrate having a non-nucleation surface (S NDS ) with small nucleation density and a nucleation surface (S NDL ) with larger nucleation density (ND L ) than the nucleation density (ND S ) of said non-nucleation surface (S NDS ) and a large area sufficient for a number of nuclei to be formed and forming selectively a II-VI group compound film only on said nucleation surface (S NDL ).

This application is a division of application Ser. No. 07/686,868, filed Apr. 16, 1991, now U.S. Pat. No. 5,100,691, which in turn, is a continuation of application Ser. No. 07/587,162, filed Sep. 21, 1990, now abandoned, which in turn, is a continuation of application Ser. No. 07/174,381, filed Mar. 28, 1988, now abandoned..

BACKGROUND OF THE INVENTION

1. Field of the Invention

This invention relates to a process for selective formation of a deposited film, particularly to a selective formation process for forming a deposited film of a II-VI group compound in a self-alignment fashion.

The selective formation process of a deposited film according to the present invention is applicable for, for example, preparation of thin films to be used for semiconductor integrated circuits, optical integrated circuits, etc.

2. Related Background Art

FIGS. 1A-1E illustrate the steps of the process for forming a thin film by photolithography of the prior art.

First, a substrate 1 comprising a material species with uniform composition as shown in FIG. 1A is washed, and then a thin film 2 is deposited on the whole surface of the substrate 1 according to various thin film depositing methods (vacuum vapor deposition method, sputtering method, plasma discharging method, MBE method, CVD method, etc.) (FIG. 1B).

Subsequently, on the thin film 2 is applied a photoresist 3 (FIG. 1C), and the photoresist 3 is exposed to light by use of a photomask of a desired pattern and the photoresist 3 is removed partially by development (FIG. 1D).

With the remaining photoresist 3 as the mask, the thin film 2 is etched to form a thin film 2 with a desired pattern (FIG. 1E).

By repeating such photolithographic steps, thin films of desired patterns are laminated to constitute an integrated circuit. In that case, alignment between the thin films of the respective layers becomes an extremely important factor for the characteristics of the device. Particularly, in the case of ultra-LSI where precision of submicron is demanded, precision of the shape of thin films of the respective layers is also extremely important along with alignment.

However, in the above process for forming a thin film of the prior art, it is difficult to effect necessary alignment of the photomasks with good precision, and also the precision of shape is insufficient, because thin films of desired patterns are formed by etching.

FIGS. 2A-2D illustrate the steps of the process for forming a thin film by use of lift-off of the prior art.

First, a photoresist 4 is applied on a substrate 1 (FIG. 2A), and the photoresist 4 with a desired pattern is removed by photolithography (FIG. 2B).

Subsequently, a thin film 5 is deposited according to a thin film deposition method (FIG. 2C), and the remaining photoresist 4 is dissolved away. By this operation, the thin film on the remaining photoresist 4 is removed at the same time, whereby a thin film 5 with a desired pattern is formed. By repeating the above steps, an integrated circuit is constituted.

However, such a thin film forming process, because a thin film is formed on a photoresist, requires to perform deposition of a thin film at a temperature not higher than the resistant temperature of the photoresist, whereby the deposition method is greatly restricted. Also, in removing the photoresist, the shape of the remaining thin film is influenced thereby and therefore precision of the shape becomes insufficient. Also, there is also the problem that the side wall or the inner portion of the thin film may be highly probably contaminated with carbon, etc. which is the component of the photoresist, etc.

Also, as the selective deposition method, there has been known the method in which a monocrystal substrate is covered partially with an amorphous thin film, and the same material as the substrate material is epitaxially grown selectively only at the exposed portion of the monocrystal substrate. For example, there are the selective epitaxial growth (SEG) method in which a silicon monocrystal substrate is partially covered with silicon oxide to effect selective growth of silicon (B. D. Joyce & J. A. Baldrey, Nature vol. 195,485, 1962), the method in which a GaAs substrate is covered partially with an amorphous thin film such as SiO₂, Si₃ N₄, etc. to effect selectively epitaxial growth of GaAs (P. Rai-Choudhury & D. K. Schroder, J. Electrochem. Soc., 118, 107, 1971), etc.

However, these selective deposition methods, because of growing selectively the monocrystal semiconductor of the same kind from the exposed surface of a monocrystal substrate, are limited in the deposition surface for the base to monocrystalline semiconductors, and therefore not applicable to polycrystalline substrates, or amorphous insulating substrates.

Thus, the deposited film forming method of the prior art is limited in available substrates, and further there are involved problems also in shape of the pattern, dimensional precision of the deposited film formed.

SUMMARY OF THE INVENTION

An object of the present invention is to solve such problems of the prior art and provide a process for forming a II-VI group compound film with any desired shape in a self-alignment fashion at any desired portion of a substrate, irrespectively of the crystallinity of the base substrate.

According to the present invention, there is provided a process for forming a II-VI group compound film comprising applying a compound film forming treatment, in a gas phase including a starting material for supplying the group II atoms of the periodic table and a starting material for supplying the group VI atoms of the periodic table, on a substrate having a non-nucleation surface (S_(NDS)) with small nucleation density and a nucleation surface (S_(NDL)) with larger nucleation density (ND_(L)) than the nucleation density (ND_(S)) of said non-nucleation surface (S_(NDS)) and a large area sufficient for a number of nuclei to be formed, and forming selectively a II-VI group compound film only on said nucleation surface (S_(NDL)).

BRIEF DESCRIPTION OF THE DRAWINGS

FIGS. 1A-1E illustrates the steps showing a thin film forming process according to photolithography of the prior art.

FIGS. 2A-2D illustrates the steps showing a thin film forming process by use of lift-off of the prior art.

FIG. 3 is a line diagram showing the relationship between the change ΔG in free energy G and the radius of nucleus.

FIGS. 4A-4D illustrates schematically the process for selective formation of a deposited film according to the present invention.

FIGS. 5A-5E illustrates the steps showing an example of selective formation of a CdSe film.

FIG. 6A-6F are preparation steps of a CdSe thin film transistor using the process of the present invention.

FIGS. 7A-7E illustrates the steps showing another example of selective formation of a CdSe film.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

The II-VI group compounds to be used in the present invention are not limited to 2-element compounds, but also include multi-element II-VI group mixed crystal compounds of 3 elements or more.

Generally, the deposited film formation process is considered, as follows.

When the substrate having a deposition surface is a material different in kind from the flying atoms, particularly an amorphous material, the flying atoms will be freely diffused on the substrate surface, or revaporized. And, as the result of collision mutually between the atoms, a nucleus is formed, and when the nucleus reaches the size rc where the change ΔG in its free energy G becomes the maximum (stable nucleus) or more, ΔG is reduced and the nucleus continues to grow stably three-dimensionally and becomes shaped in an island form.

The change ΔG in free energy G created by formation of nucleus is represented as follows:

    ΔG=4πf(θ)(σ.sub.o r.sup.2 +1/3·gv·r.sup.3)

    f(θ)=1/4(2-3 cosθ+cos.sup.2 θ)

where r: radius of curvature of nucleus

θ: contact angle of nucleus

gv: free energy per unit volume

σ_(o) : surface energy between nucleus and vacuum.

The manner in which ΔG is changed is shown in FIG. 3. In FIG. 3, the radius of curvature of the stable nucleus when ΔG is at the maximum value is rc.

Thus, the nucleus grows to become shaped in an island form, and further grows until contact mutually between islands proceeds to cover the substrate surface in the shape of a network, finally covering completely the substrate surface as a continuous film. Through such process, a thin film is deposited on the substrate.

In the deposition process as described above, the density of the nucleus formed per unit area of the substrate surface depends greatly on the interaction between the flying atoms and the substrate, and is also greatly influenced by the deposition conditions, typically the temperature.

Accordingly, by selecting appropriately the kinds of the material for the deposited film and the substrate material, and setting appropriately the deposition conditions such as temperature, pressure, gas species, etc., the nucleation density (or nucleation speed) can be determined. Therefore, when one kind of material to be deposited is used and deposits on a deposition surface comprising two or more kinds of surfaces differing greatly in the above nucleation density, the deposited film can be formed selectively depending on the difference of nucleation density. For example, it is formed selectively as described below.

FIGS. 4A-4D illustrate schematically the process of forming a deposited film according to the present invention.

First, the two kinds of materials constituting the deposition surface are called A and B, and the material to be deposited C, and the above materials A, B and C are selected so that the nucleation density of the material to be deposited C for the materials A and B may differ greatly, under certain deposition conditions. Here, it is supposed that the nucleation density for the material A is sufficiently great, and the nucleation density for the material B is negligibly small.

In FIG. 4A, on a substrate 1 of a material resistant to high temperatures such as high-melting glass, quartz, alumina, ceramics, etc., a thin film 6 of the material B is deposited according to a thin film forming method, and ions of the material A are implanted with a desired pattern by use of the converging ion beam implantation technique thereon. By this process, as shown in FIG. 4B, a region 7 of the material A is formed with a desired pattern so as to have a large area sufficient for a number of nuclei for crystal growth to be generated on the thin film 6 of the material B.

Thus, as the method for forming the region 7 constituted of the material A with a desired pattern on she deposition surface, as shown in FIG. 4C, a mask may be formed with a desired pattern on the material B, and ions of the material A injected on the whole surface to provide the region 7, thereby forming a deposition surface as shown in FIG. 4B.

Also, a thin film of the material A may be formed on the material B, and the thin film of the material A may be formed to a desired pattern by photolithography.

As shown in FIG. 4B, on the deposition surface constituted of the material A and the material B to a desired pattern, the material C is deposited under predetermined conditions. At this time, no material C is deposited on the thin film 6 of the material B.

This may be considered to be due to revaporization of the flying atoms of the material C before becoming stable nucleus, or due to formation of a substance with high vapor pressure through the reaction of C atoms with the material B, whereby the material B is etched.

Thus, only on the region 7 of the material A, the material C is deposited, and consequently a deposited film 9 with same pattern as the pattern of the region 7 of the material A can be formed in a self-alignment fashion.

The present invention is described in more detail below by referring to Examples along with the drawings.

EXAMPLE 1

Referring to FIGS. 5A-5E, the process for forming a CdSe film on SiO₂ is described as a first example of the present invention.

On a substrate 1 resistant to high temperature comprising alumina, a SiO₂ film 10 was deposited to about 1000Å by conventional CVD (chemical vapor deposition) by use of silane (SiH₄) and oxygen (O₂) [FIG. 5A]. The nucleation density (NDs) of CdSe on the SiO₂ film is small, and the SiO₂ film 10 becomes the non-nucleation surface (S_(NDS) ).

Next, the surface of the SiO₂ film 10 was masked with a photoresist 11 to a desired pattern. [FIG. 5B]

By use of an ion implanter, Se ions 12 were implanted at a density of 3×10¹⁶ /cm². The Se ions were implanted only on the surface exposed [FIG. 5C]. At the SiO₂ film surface 13 where no Se ion is implanted, the nucleation density (NDs) of CdSe is small, and this portion becomes the non-nucleation surface (S_(NDS)) as described above. On the other hand, the region 14 where Se ions are implanted has larger nucleation density (ND_(L)) than the non-nucleation surface (S_(NDS)), which portion becomes the nucleation surface (S_(NDL)). The size of the region 7 was made 1 mm ×1 mm square.

After the photoresist was peeled off, the substrate 1 was subjected to heat treatment in a PCl₃ atmosphere at about 450° C. for about 10 minutes to clean the surface [FIG. 5D].

Subsequently, while the substrate 1 was heated to 500 ° C., diethyl cadmium (DECd) and selenium hydride (H₂ Se) at a molar ratio of 1:5 were flowed together with a carrier gas H₂ onto the substrate surface to grow a CdSe film according to the MOCVD (organometallic chemical vapor deposition) method. The reaction pressure was made 10 Torr. As shown in FIG. 5E, CdSe film 15 was formed only on the nucleation surface (S_(NDL)) 14 formed by implantation of Se ions, and no CdSe film was formed on the nonnucleation surface (S_(NDS)) 13, namely the SiO₂ surface where no Se ion was implanted.

Accordingly, as can be seen from the above, by implantation of Se ions with a desired pattern, a CdSe film with any desired shape and dimension can be selectively formed.

EXAMPLE 2

Referring to FIG. 6, preparation steps of a CdSe thin film transistor as an example of the present invention are described.

First, an Al film was deposited on an alumina substrate 1 to about 1000Å according to the vacuum vapor deposition method, followed by patterning by conventional photolithographic technique to form a gate electrode 16 [FIG. 6A].

Next, according to the sputtering method, a SiO₂ film 17 was deposited to about 3000Å to give a gate oxide film [FIG. 6B].

With the SiO₂ film 17 being masked with a photoresist 18, Se ions 19 were implanted into the SiO₂ film only at the transistor forming region by use of an ion implanter. The amount implanted was 3×10¹⁵ /cm². Thus a nucleation surface (S_(NDL)) 20 having a large nucleation density (ND_(L)) was formed [FIG. 6C].

After the photoresist was peeled off, the surface was cleaned by subjecting it to the heat treatment in PCl₃ atmosphere at about 450° C. for about 10 minutes. Next, a CdSe film was grown selectively according to the MOCVD method. By use of diethyl cadmium (DECd) and H₂ Se as the starting gases, both were fed at a mixing ratio of 1:5 (molar ratio) together with a carrier gas H₂ onto the substrate. It has been found that at this time, crystallinity of CdSe to be formed can be improved by addition of 1 to 2% of HCl in the carrier gas H₂. The reaction pressure was made 30 Torr, and the substrate temperature 450° C. Thus, as shown in FIG. 6D, the SiO₂ surface having small nucleation density (NDs) became the non-nucleation surface (S_(NDS)), and the ion implanted portion having larger nucleation density (ND_(L)) became the nucleation surface (S_(NDL)), whereby CdSe 21 was formed selectively only on the nucleation surface (S_(NDL) ) 20.

Next, an Al film 22 was formed by vacuum vapor deposition on the whole surface of the SiO₂ film and the CdSe film 20. [FIG. 6E].

Finally, according to photolithographic technique, the Al film was worked to form the source electrode 23 and the drain electrode 24, thus completing a thin film transistor [FIG. 6F].

Thus, according to the process of the present invention, since a CdSe film can be formed selectively only on the nucleation surface (S_(NDL)), a thin film transistor can be prepared without chemically etching CdSe as different from the prior art method. For this reason, thin film transistors of good quality could be prepared with good yield, as compared with the prior art method.

EXAMPLE 3

FIGS. 7A-7E illustrate the film formation steps of another example of the present invention.

First, similarly as in Example 1, on the surface of a substrate 1 resistant to high temperature comprising alumina, a SiO₂ film 25 was deposited about 1000 Åaccording to the CVD method by use of SiH₄ and O₂ [FIG. 7A].

Next, by means of an arc discharge type ion plating device, on the SiO₂ film 25 was formed an Al₂ O₃ film. After the device was internally evacuated to 10⁻⁵ Torr, O₂ gas was introduced to 3×10₋₄ Torr, and an Al₂ O₃ film 26 was deposited to about 300Å on the substrate heated to 400° C. at an ionization voltage of 50 V, a substrate potential of -50 V and an output of 500 W [FIG. 7B].

With a photoresist 27 masked to a desired pattern on the Al₂ O₃ film 26, the portion of the Al₂ O₃ film exposed was etched with an etchant of H₃ PO₄ :HNO₃ :CH₃ COOH:H₂ O=16:1:2:1 [FIG. 7C]. At this time, the substrate was heated to about 40° C.

After the photoresist 27 was peeled off, the substrate 1 was subjected to heat treatment in a PCl₃ atmosphere at about 450° C. for about 10 minutes to clean the surface [FIG. 7D]. On the SiO₂ surface nucleation density (NDs) of CdSe is small, which portion becomes the non-nucleation surface (S_(NDS)). On the other hand, Al₂ O₃ film 26 has larger nucleation density (ND_(L)) than the non-nucleation surface (S_(NDS)) 25, which portion becomes the nucleation surface (S_(NDL)).

Subsequently, while the substrate 1 was heated at 450° C., diethylcadmium (DECd) and selenium hydride (H₂ Se) at a molar ratio of 1:5 were flowed together with a carrier gas H₂ onto the substrate surface to grow a CdSe film according to the MOCVD (organometallic chemical vapor deposition) method. The reaction pressure was made about 30 Torr. As shown in FIG. 7E, CdSe film 28 was formed only on the Al₂ O₃ nucleation surfaces (S_(NDL)) 26, and no CdSe film was formed on the non-nucleation surface (S_(NDS)) 25, namely the SiO₂ surface. The size of the nucleation surface (S_(NDL)) 26 was made 1 mm×1 mm square.

Thus, also according to the process of this Example, it could be confirmed that a CdSe film with any desired shape and dimension was selectively formed on any desired substrate.

EXAMPLE 4

A ZnSSe mixed crystal II-VI group compound film was selectively formed as follows.

After deposition of a SiO₂ film to about 1000Å on an alumina substrate 1 according to the CVD method by use of SiH₄ and O₂ in the same manner as in Example 1, with a photoresist masked to a desired pattern on the surface, Se ions were implanted into the exposed SiO₂ at 1×10¹⁵ /cm² by use of an ion implanter.

Next, the resist film was peeled off, and the substrate 1 was subjected to heat treatment in a PCl₃ atmosphere at about 450° C. for about 10 minutes to clean the surface.

Also for the ZnSSe mixed crystal, the SiO₂ film portion implanted with no Se ions has smaller nucleation density (NDs) to become the non-nucleation surface (S_(NDS)). On the other hand, the SiO₂ film portion implanted with Se ions has larger nucleation density (ND_(L)) to become the nucleation surface (S_(NDL)).

Onto the substrate surface having the nucleation surface (S_(NDL)) and the non-nucleation surface (S_(NDS)) thus having a nucleation density difference (ΔND), by use of H₂ as the carrier gas, dimethylzinc (DMZ), dimethylselenium (DMSe) and diethylsulfur (DES) were flowed at a ratio of DMZ: (DMSe+DES) of 1:8 (molar ratio). The substrate temperature was made 500° C. by heating. The reaction pressure was made 100 Torr. Similarly as shown in FIG. 5E, only on the nucleation surface (S_(NDL)) formed by implantation of Se ions, the ternary mixed crystal II-VI group compound ZnSSe film was formed selectively. In this case, the size of the nucleation surface (S_(NDL)) was made 1 mm×0.5 mm square.

The ratio of S and Se in ZnSSe can be freely controlled by varying the ratio of the reactive gases DES and DMSe.

EXAMPLE 5

A chalcopyrite type compound film with the group II element in the II-VI compound substituted with the group I element and the group III element was formed as follows.

Similarly as in the respective examples described above, a SiO₂ film was formed on the substrate, and Se ions were partially implanted thereon similarly as in Example 1 to form a nucleation surface (S_(NDL)). In this example, as in Example 3, an Al₂ O₃ film may be formed on SiO₂ film, followed by patterning to form a nucleation surface (S_(NDL)). A chalcopyrite film was selectively formed according to the MOCVD method only on the fine nucleation surface (S_(NDL)) on the substrate having the non-nucleation surface (S_(NDS)) and the nucleation surface (S_(NDL)). In the case of forming a CuGaS₂ film, cyclopentadienyltriethylphosphine copper [C₅ H₅ CUP(C₂ H₅)₃ ], trimethylgallium (TMG) and hydrogen sulfide (H₂ S) were supplied as the reactive gases together with the carrier gas H₂ onto the substrate. C₂ H₅ CuP(CH₂ H₅)₃ and TMG were supplied in equal moles, with the amount of H₂ S being made about several-fold of the sum of the former two. The reaction pressure was made 50 Tort, and the substrate temperature 600° C. Thus, CuGaS₂ could be formed selectively only on SiO₂ implanted with Se ions.

As shown in the above Examples, according to the present invention, a nucleation surface (S_(NDL)) having a large nucleation density (ND_(L)) can be formed to a desired pattern and a II-VI group compound semiconductor film following the pattern can be formed.

In the above Examples, there are shown examples of forming a SiO₂ film by the CVD method, but it is also possible to form a SiO₂ film by the sputtering method. Further, quartz with its surface well flattened itself can be also used as the deposition surface.

The ion species to be implanted for formation of the nucleation surface (S_(NDL)) is not limited to Se ions, but ions of the group If elements, ions of the group VI elements, further ions of the group III elements and ions of the group V elements can be also used.

By use of dimethylzinc, diethylzinc [Zn(C₂ H₅)₂ ], dimethylcadmium [Cd(CH₃)₂ ], diethylcadmium, dipropylcadmium [Cd(C₃ H₇)₂ ], dibutylcadmium [Cd(C₄ H₉)₂ ], dimethylmercury [Hg(CH₃)₂ ], diethylmercury [Hg(C₂ H₅)₂ ] as the starting gas of the group II element, and hydrogen sulfide (H₂ S), selenium hydride, dimethylselenium, diethylselenium [Se(C₂ H₅)₂ ], dimethyldiselenide [CH₃ SeCH₃ ], dimethyltellurium [Te(CH₃)₂ ], diethyltellurium [Te(C₂ H₅)₂ ] as the starting gas of the group VI element, films of II-VI group compounds ZnS, ZnTe, CdS, CdTe, HgSe and mixed crystal compound films thereof can be formed according to the combinations of these selectively on the nucleation surface (S_(NDL)). Selective formation of a ZnO film is also possible.

A mixed crystal compound semiconductor can be formed selectively on Al₂ O₃ provided an the similarly as in Example 2 as the nucleation surface (S_(NDL)), as a matter of course.

Further, in the respective Examples as described above, examples in which the MOCVD method is used in the step of selective formation of a CdSe and a ZnSSe films have been shown, but selective formation of the II-VI group compound film of the present invention can be also practiced according to entirely the same principle by use of MBE (molecular beam epitaxy) method, LPE (liquid phase growth) method, etc.

As described in detail above, the process for selective formation of a II-VI group compound film can form self-matchingly a deposited film of a desired pattern by utilizing the nucleation density difference (ΔND) depending on the kinds of the II-VI group compound deposition surface materials, and therefore a deposited film with a desired pattern can he formed at high precision, which is advantageous particularly in constituting a highly integrated circuit. Further, the materials of the deposition surface are not required to be limited to only monocrystal but a II-VI group compound deposited film can be formed at high precision also on an amorphous insulating material by selecting the material for forming nucleation surface (S_(NDL)) and the material for forming non-nucleation surface (S_(NDS)) having nucleation density difference.

Particularly, in the case of a compound semiconductor with large influence by chemical etching, a pattern can be formed without etching of the film itself, and therefore it becomes possible to maintain chemical stability of the film prepared at high level. 

We claim:
 1. A semiconductor device having a II-VI group compound film, which comprises:a substrate; a first electrode provided on said substrate; a polycrystalline or amorphous insulating film provided on said first electrode having a non-nucleation surface with small nucleation density and a nucleation surface with larger nucleation density than the nucleation density of said non-nucleation surface and a large area sufficient for a number of nuclei to be formed; a II-VI group compound film on said nucleation surface formed by applying a II-VI group compound film forming treatment on said insulating film; and a second electrode provided in contact with said II-VI group compound film.
 2. A device having a II-VI group compound film according to claim 1, wherein said II-VI group compound film is a binary system II-VI group compound film.
 3. A device having a II-VI group compound film according to claim 1, wherein said II-VI group compound film is at least a ternary multi-component system mixed crystal II-VI group compound film.
 4. A device having a II-VI group compound film according to claim 1, wherein the group II atoms in the II-VI group compound are substituted with group I atoms and group III atoms.
 5. A device having a II-VI group compound film according to claim 1, wherein the nucleation surface (S_(NDL)) is formed by selective ion implantation onto said insulating film.
 6. A device having a II-VI group compound film according to claim 1, wherein the nucleation surface is formed by deposition of a nucleation surface forming substance having a large nucleation density (NDL) on a part of said non-nucleation surface (S_(NDS)).
 7. A device having a II-VI group compound film according to claim 1, wherein said non-nucleation surface is comprised of an amorphous insulating material.
 8. A device having a II-VI group compound film according to claim 7, wherein said amorphous insulating material is SiO₂.
 9. A device having a II-VI group compound film according to claim 6, wherein said non-nucleation surface and said nucleation surface are constituted of SiO₂ and Al₂ O₃, respectively.
 10. A device having a II-VI group compound film according to claim 1, wherein said II-VI group compound film-forming treatment is the MOCVD method. 